AMPLIFY™ GR 216

Category:	MAH-g , Functional Polymer
Manufacturer:	The Dow Chemical Company
Trademark:	AMPLIFY™ GR
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zAAE7B_AMPLIFY-GR-216.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

AMPLIFY™ GR 216 Functional Polymer is a maleic anhydride grafted (MAH) polymer. The base polymer is a polyolefin elastomer with high flexibility and elasticity.

Main Characteristics:

High elasticity with good elastic recovery

Excellent impact strength in blends with polyamide and other engineering resins

Maleic anhydride grafted elastomer

Polymer compatibilizer

Impact Modification

Adhesion promoter

Promotes adhesion between metal , polyolefins, cellulose, polyester, polycarbonate, glass and foil.

-Useful to improve impact resistance of polyamides and other engineering resins.

Complies with:

U.S. FDA 21 CFR 175.105

EU, No 10/2011

Consult the regulations for complete details.

General Information
Agency Ratings	FDA 21 CFR 175.105 Europe No 10/2011
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	0.875	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ASTM D1238, ISO 1133
MAH Graft Level ¹	High		Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness			ASTM D2240, ISO 868
Shaw A	77		ASTM D2240, ISO 868
Shaw D	21		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	8.96	MPa	ASTM D638, ISO 527-2/51
Tensile Elongation (Break)	1000	%	ASTM D638, ISO 527-2/51
Flexural Modulus - 2% Secant	13.8	MPa	ASTM D790A, ISO 178

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-53.9	°C	Internal method
Vicat Softening Temperature	40.0	°C	ASTM D1525, ISO 306
Melting Temperature (DSC)	62.8	°C	Internal method

Additional Information
根据 ASTM D4976 进行模塑。

Note Message
1 .	Low:<0.25 wt %, medium 0.25-0.5 wt %, high> 0.5 wt%.

Resin Grade	Manufacturer	Category	Trademark
Next ABS SXT4-02ABK	Next Polymers Ltd.	ABS	Next ABS
Cheng Yu ML3410	Cheng Yu Plastic Company Limited	PC	Cheng Yu
Geon™ Vinyl Rigid Molding M3400	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Rigid Molding
LNP™ THERMOCOMP™ JF004Z compound	SABIC Innovative Plastics Europe	PESU	LNP™ THERMOCOMP™
EPALINE 386A11	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPALINE