Star X 1615 33V S4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Star X |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z9gwxk_Star-X-1615-33V-S4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Star X 1615 33V S4 is an Impact Modified, Glass Fiber Reinforced , UV stabilized Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.10 to 0.40 | % | Internal Method |
| Ash Content (650°C) | 33 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 to 6.0 | % | ISO 527-2 |
| Flexural Modulus | 6100 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 2(23°C) | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 85 | kJ/m² | |
| 23°C | 90 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 100 mm Span) | 230 | °C | ISO 75-2/Ae |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 sp=62mm |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ST3200-0005 ES RS | PolyOne Corporation | PC | Stat-Tech™ |
| Sup-tech CT103 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC+PBT | Sup-tech |
| ACRYLITE® H12 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| KPOL-PP K-PPH 8.5F | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| RONFALIN® ABS 1411 GF 30 | A. Schulman Europe | ABS | RONFALIN® |