Petro Rabigh PP FY4012E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z9BxgZ_Petro-Rabigh-PP-FY4012E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FY4012E is a homopolymer polypropylene intended for Yarn extrusion. Yarn made from this resin exhibits high denier strength, high anti splitting and low heat shrinkage. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 152 | °C | ASTM D1525 1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C |
| Extrusion instructions |
|---|
| Stretching Temperature: 155°CStretching Ratio: 4 to 6 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tislamid® PA66 PA66 20 GBR | Tisan | Nylon 66 | Tislamid® PA66 |
| Toyolac® TP82-X05 | Toray Resin Company | ABS | Toyolac® |
| Anjacom® 200C-UV | Almaak International GmbH | Nylon 6 | Anjacom® |
| Polifil® Nylon 625L | The Plastics Group | Nylon 66 | Polifil® Nylon |
| OTECH PVC OW134 - Automotive Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |