NEFTEKHIM PP 1510L (C30S)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z99Dt2_NEFTEKHIM-PP-1510L-C30S-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by polymerization of propylene in presence of complex organic metal catalysts. It incorporates increased long-term thermal stability, thermaloxidative degradation resistance when PP is produced, processed and PP-made articles are exploited. Application: packing cord and rope, sheets to manufacture office folders, raffia. Technical requirements: TU 2211-136-05766801-2006 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | |
| Apparent Density | 0.48 to 0.52 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 to 7.0 | g/10 min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| Gel Content 1 | |||
| > 200.0 µm | 250 | pcs/m² | |
| 0.700 to 1.50 mm | 3.00 | pcs/m² | |
| 1.50 to 2.50 mm | 0.00 | pcs/m² | |
| > 2.50 mm | 0.00 | pcs/m² |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Creep Temperature 2 | 90 to 96 | °C | |
| Thermal-oxidative Deterioration (150°C) | 15.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 to 95 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 1350 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Vicat Softening Temperature 3 | 150 to 154 | °C |
| Note Message | |
|---|---|
| 1 . | p.4.8 ?U 2211-136-05766801-2006 |
| 2 . | at load 0.46 H/mm² |
| 3 . | in liquid medium under force 10 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1032H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sasol Polymers PP ESV200 | Sasol Polymers | PP Random Copolymer | Sasol Polymers PP |
| TYNEA 3902 | Tyne Plastics LLC. | Acetal (POM) Homopolymer | TYNEA |
| Abstron IM17AHF | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Latistat 63-08 | LATI S.p.A. | Nylon 6 | Latistat |