ALPHALAC SF510
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | ALPHALAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z8Abse_ALPHALAC-SF510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alphalac of LG chemical is high functionality styrene resin and offers excellent properties and processibility .This product can be accepted as the replacement of general ABS resins. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1670 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus 4 | 2240 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 39.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 49 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35mm | 85.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 6.35mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 6.35mm | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 6 |
| -- | 86.0 | °C | ASTM D1525 7 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Flammability, IEC 707, 1/8 in, mm/min: FH3-28 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 205 - 220 | °C | |
| Front Temperature | 215 - 230 | °C | |
| Nozzle Temperature | 205 - 230 | °C | |
| Processing (Melt) Temp | 215 - 230 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa | |
| Holding Pressure | 50.0 - 80.0 | MPa | |
| Back Pressure | 10.0 - 30.0 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 50 mm/min |
| 6 . | 压 力1 (10N) |
| 7 . | 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURACON® GH-25LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| EcoVid 30GBIM | Greener Polymers Inc. | PLA | EcoVid |
| LNP™ STAT-KON™ ME006 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |
| Lupolen 2427 F | LyondellBasell Industries | LDPE | Lupolen |
| OTECH PVC OW635 AFR - Riser Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |