VECTRA® FIT70
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z87RYn_VECTRA-FIT70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
35% glass and mineral reinforced grade. It offers excellent flowability, low warpage, excellent surface appearance, excellent dimensional stability, and good weldline strength. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.43 | % | ISO 294-4 |
| Flow direction | 0.050 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Flexural Strain at Break | 2.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 278 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | °C | ISO 75-2/A |
| Melting Temperature 1 | 331 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 330 - 350 | °C | |
| Nozzle Temperature | 330 - 340 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Zone 4 Temperature: 330 to 350°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® P K40T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| BESTPOM H02/01 | Triesa Plastics | Acetal (POM) Homopolymer | BESTPOM |
| Sylvin 8290-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DEXFLEX® E756-1 BLK | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| LNP™ THERMOCOMP™ CF008 compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ THERMOCOMP™ |