LNP™ LUBRICOMP™ UCP36S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z7IsXb_LNP-LUBRICOMP-UCP36S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* UCP36S is a compound based on PPA resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound UCL-4536 HS Product reorder name: UCP36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.11 | % | |
| Across Flow : 24 hr | 0.72 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.26 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 26400 | MPa | ASTM D638 |
| -- | 26100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 235 | MPa | ASTM D638 |
| Break | 229 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.3 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 22400 | MPa | ASTM D790 |
| -- 5 | 22200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 321 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 326 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.35 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.550 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 62 | J/m | ASTM D256 |
| 23°C 7 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 8 | 36 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.60 | J | ASTM D3763 |
| -- | 1.92 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 278 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 280 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 260 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polycarbonate PC100RULUV-18M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Gallonprene® GP210-4011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Gallonprene® GP420-5501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina ORANGE PVC COMPOUND 650-32/95 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pemex PX 22004 C | Pemex Petroquímica | LDPE | Pemex |