DOW™ LDPE 421E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z62VnS_DOW-LDPE-421E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE™421E low density polyethylene resin can be extruded by ordinary blown film process, and the melt temperature is between 160 and 195°C. When prepared, this resin has excellent mechanical properties even at a higher density (high stiffness) than a standard resin, while maintaining very high transparency and gloss. This resin has good drafting and processability. This product does not contain slip agent or opening agent. regulatory requirements: DOW LDPE 421E low density polyethylene resin shall meet the following regulatory requirements: us food and drug administration regulation 21 CFR 177.1520(c)2.2 EU, No 10/2011 please consult the regulations for complete details. Application field:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 50 µm | 290 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm | 250 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 11.0 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 19.0 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 15.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 420 | % | ISO 527-3 |
| TD : Break, 50 µm | 550 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 100 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 500 | g | ASTM D1922 |
| TD : 50 µm | 350 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 195 | °C |
| Extrusion instructions |
|---|
| 放大比 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pomalux® Unfilled | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| ROPOTEN® FV-2-109 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® |
| HiFill® PP 0112 B | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Hylex® P1025G20FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Plaslube® PA6 GF40 ML5 HS 12MM | Techmer Engineered Solutions | Nylon 6 | Plaslube® |