HAIPLEN EP30 Z1 G6 BA
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5oQTK_HAIPLEN-EP30-Z1-G6-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer glass fiber reinforced 30% chemical coupled, very high impact strength also at low temperature. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.35 to 0.50 | % | |
| Across Flow | 0.60 to 0.75 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 70.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | > 150 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 100 | °C | ASTM D1525, ISO 306/B 3 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G30 N10 NTLA010 NR314 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Estane® ETE 60DS3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Hylex® P1017FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| LEXAN™ 940 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Plaslube® POM CO E TL20 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |