Order Products : sales@su-jiao.com
Latistat 52/7-02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latistat |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5XZfG_Latistat-52-7-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dissipative product based on Polypropylene homopolymer (PPh). |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.6 to 1.9 | % | |
| Flow : 2.00 mm | 1.5 to 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.0 | % | |
| Break, 23°C | 3.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 20 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 50 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8215-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AIE PA66 60G6F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Ferro PP NPP00GDV04WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Elastron® G G100.A65.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Sylvin 83042-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |