Order Products : sales@su-jiao.com
LTP ZW-3150
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | Chengdu Letian Plastics Co., Ltd |
| Trademark: | LTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5MFcb_LTP-ZW-3150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resin of LTP ZW-3000 serials is crystal whisker reinforced materials with wear-resisting property based on high molecular weight linear PPS. Its characteristics are as following: (1)elevated temperature property: long run under 180-220°C; (2)self-lubricating property: work for long time without any lubrication additive under usage temperature; (3)resistance to solvent: not swelling in oil, organic solvent, especially in gasoline, diesel oil, alcohols and aromatic series esters; (4)high thermal conduction: the heat by friction can transfer through metal parts or air when used under elevated temperature? As high strength and low density in one, Resin of LTP ZW-3000 serials are broadly applied as wear resisting parts under elevated temperature and humidity work conditions for aerospace, automotive, machine, household appliances, petroleum and chemical industry, such as bearing, axile bush, gear wheel, impeller blade, belt roller, brake block and so on. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 to 1.82 | g/cm³ | GB/T 1033 |
| Melt Mass-Flow Rate (MFR) | 20 to 120 | g/10 min | GB/T 3682 |
| Molding Shrinkage 1 | |||
| Across Flow : 3.00 mm | 0.30 to 0.50 | % | |
| Flow : 3.00 mm | 0.20 to 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 to 0.40 | % | GB/T 1034 |
| PV Limit | 800 to 1600 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wear Factor 2 | 0.00200 to 0.100 | mm³/kg/km |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 245 to 270 | °C | GB/T 1634 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 to 120 | GB/T 9342 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 150 | MPa | GB/T 1040 |
| Tensile Strain (Break) | 0.60 | % | GB/T 1040 |
| Flexural Stress | 180 | MPa | GB/T 1042 |
| Compressive Stress | 220 | MPa | GB/T 1041 |
| Coefficient of Friction (Dynamic) | 0.10 to 0.30 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | GB/T 1043 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+14 | ohms | GB/T 1410 |
| Volume Resistivity | 1.0E+10 to 1.0E+13 | ohms·cm | GB/T 1410 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 mm |
| 2 . | 45# Steel |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® FU1007 | Covestro - Polycarbonates | PC | Makrolon® |
| Pomalux® 25% GF | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| Telcar® SGE60050 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Lupoy® GN1002FC | LG Chem Ltd. | PC | Lupoy® |
| Sylvin 8386-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |