NORYL™ PN275F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5APO9_NORYL-PN275F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS with low mineral loading. High heat, platable applications. NSF approved for water contact applications. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 5.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 55.2 | MPa | |
| Break | 48.3 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.6 | % | |
| Break | 34 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 44.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 137 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 121 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Nozzle Temperature | 282 to 310 | °C | |
| Processing (Melt) Temp | 282 to 310 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 1252F | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Geon™ Vinyl Dry Blend E6530 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| ELASTOSIL® R 756/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Globalene® SH3302 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Karina WHITE COLOR CONCENTRATE 10/105-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |