Zytel® PLUS PLS95G35DH1 NC010
| Category: | Nylon, Unspecified , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z4TkOK_ZytelPLUSPLS95G35DH1NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Heat Stabilized, Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 20.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.60 | -- | % | ISO 294-4 |
| Flow | 0.10 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 209 | 148 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | 5.4 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 76 | 96 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 249 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 265 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 280 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 275 - 285 | °C | |
| Mold Temperature | 70 - 120 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B40 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| CALP FR970-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| GAPEX® RPP30EU67BK BLACK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Electrafil® J-1/CF/10 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| OmniCarb™ PC08FR GF20 | OMNI Plastics, LLC | PC | OmniCarb™ |