MFE® -9

Category:	Vinyl Ester , Vinyl Ester
Manufacturer:	Huachang Polymer Co., Ltd.
Trademark:	MFE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	z3sNtM_MFE--9.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MFE-9 Vinyl Ester Resin is a rubber modified resin with high toughness, and based on Bisphenol-A epoxy vinyl ester resin.

PROPERTY

Low solid contractibility, high toughness, high ductility

Excellent fatigue resistance, impact resistance and cleavage resistance

Excellent adhesion and abrasion resistance, excellent impact strength.

Excellent penetration-proof and hermetically seal.

APPLICATION

Used in making flooring, daubing material, sealing material and interface layer of FRP lining

Used in manufacturing helmet for aviation, automobile race and military use, short sled, sailing boat and high performance racing boat

Excellent adhesion, can be used for special tackiness agent

Used with fiber and other reinforced materials, give excellent strength and fatigue resistance property to lamination

General Information
Additive	Rubber
Features	Ductile Fatigue Resistant Good Adhesion Good Toughness Heat Sealable High Impact Resistance Puncture Resistant
Uses	Adhesives Automotive Applications Flooring Maintenance/Repair Laminates Safety Helmets Sealants
Appearance	Yellow

Physical	Nominal Value	Unit
Solids Content	55 to 63	%

Thermal	Nominal Value	Unit	Test Method
Thermal Stability (80°C)	> 1	day

Thermoset	Nominal Value	Unit
Gel Time (25°C)	22.0 to 38.0	min

Additional Information	Nominal Value	Unit
Peak Exotherm	120 to 140	°C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2400	MPa	ASTM D638
Tensile Strength	60.0	MPa	ASTM D638
Tensile Elongation (Break)	11	%	ASTM D638
Flexural Modulus	2800	MPa	ASTM D790
Flexural Strength	110	MPa	ASTM D790
Compressive Strength	115	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	25.0	kJ/m²	ASTM D6110

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	80.0	°C	ASTM D648

Thermoset	Nominal Value	Unit
Thermoset Mix Viscosity (25°C)	300 to 500	cP

Resin Grade	Manufacturer	Category	Trademark
G-Lene PB48A004	Gas Authority of India Limited	HDPE	G-Lene
Lifoflex® UVX 40.01 B038-8	ELASTO	TPE	Lifoflex®
Karina CLEAR PVC COMPOUND -E 75/244-D-AT-IS-SI	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 7011EE-60 BLACK	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
KMI PE LDPE REPRO	KMI Group, Inc.	LDPE	KMI PE