LNP™ LUBRICOMP™ OCP36A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z3PeLm_LNPLUBRICOMPOCP36Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OCL-4536 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Internally Lubricated, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound OCL-4536 Product reorder name: OCP36A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.49 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.66 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.15 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 18600 | MPa | ASTM D638 |
| -- | 19900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 128 | MPa | ASTM D638 |
| Yield | 113 | MPa | ISO 527-2 |
| Fracture | 119 | MPa | ASTM D638 |
| Fracture | 113 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 0.90 | % | ASTM D638 |
| Yield | 0.77 | % | ISO 527-2 |
| Fracture | 1.6 | % | ASTM D638 |
| Fracture | 0.78 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 20100 | MPa | ASTM D790 |
| -- | 19000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 230 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.36 | ASTM D3702 Modified | |
| With Self-Static | 0.30 | ASTM D3702 Modified | |
| Wear Factor - Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 3.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D4812 |
| 23°C 3 | 14 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.30 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 274 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 272 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 259 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 248 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.2E-6 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.0E-6 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 271GA | INOVYN | PVC, Unspecified | SolVin |
| Vydyne® R525H BK02 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| PIVINEL™ 126-D1 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| Sumiliteresin® PR-51587 I | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 9077-85 Grey 9470 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |