MAJORIS PBT 9383 30 FV halogen free
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z2ITH5_MAJORIS-PBT-9383-30-FV-halogen-free.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT 9383 30FV is a 30 % glass fibre reinforced polybutylene terephthalat, halogen free, intended for injection moulding. Classified V0 according to UL94 norm, PBT 9383 30FV is available in natural but other colours can be provided on request. This technical datasheet is valid for all our compounds PBT 9383 30FV : natural or other colours. PBT 9383 30FV combines high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability. APPLICATIONS PBT 9383 30FV is intended for the injection moulding of electrical components and automotive applications including interior, exterior and electrical and mechanical systems. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 180 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| 2.00 mm | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Back Pressure: Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3001 | RTP Company | PMP | RTP |
| S&E PVC G-95-064A | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Unichem 8312GA-05 | Colorite Polymers | PVC, Flexible | Unichem |
| Elastron® G G100.D35.B | Elastron USA, Inc. | SEBS | Elastron® G |
| EMPILON® 8890 | EMPILON | SEBS | EMPILON® |