PBT glass fibre reinforced 30% heat stabilised, self extinguishing UL94 V0 also at low thickness PBDE/PBDF free, good flow, good surface finish, good mechanical properties, very high dimensional stability good tracking resistance. UL94 V0 approved NC,BK at 0,75 mm. UL 746B approved. Available: different colours. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 to 1.66 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.030 | % | ASTM D570, ISO 62 |
| Saturation | 0.22 | % | ASTM D570 |
| Saturation, 23°C | 0.22 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 210 | MPa | ISO 178 |
| Break | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 7.0 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 130 | °C | UL 746B |
| -- 2 | 140 | °C | IEC 60216 |
| -- 3 | 165 | °C | IEC 60216 |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50, ASTM D1525 4 |
| Ball Pressure Test (215°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 to 225 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Short Term |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarMediflex P 7025-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| NITRIFLEX NTL-260 | NITRIFLEX | SBR, Unspecified | NITRIFLEX |
| Nypol® PA A3 G33 NTLA010 NR315 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LEXAN™ 925U resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LUVOCOM® 1200-7116 | LEHVOSS Group | ABS | LUVOCOM® |