ULTEM™ DU242 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z1VsDz_ULTEM-DU242-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Enhanced low temperature impact, high flow Polyetherimide blend. ECO Conforming. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2590 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 74.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 67 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2520 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 2000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 160 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 310 to 332 | °C | |
| Middle Temperature | 321 to 343 | °C | |
| Front Temperature | 332 to 354 | °C | |
| Nozzle Temperature | 327 to 349 | °C | |
| Processing (Melt) Temp | 332 to 354 | °C | |
| Mold Temperature | 93.3 to 135 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 241-73W236 | ExxonMobil Chemical | TPV | Santoprene™ |
| Stat-Tech™ AT-10CF/000 | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| GLAMIDE® T-422VOR | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| LEXAN™ EXL9414T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Lustran® SAN Sparkle | Styrolution | SAN | Lustran® SAN |