Visico™ LE4423/Ambicat™ LE4476 Datasheet,XLPE,Borealis AG-SHANGHAI SUSHENG

Visico™ LE4423/Ambicat™ LE4476

Category:	XLPE , Crosslinked Polyethylene
Manufacturer:	Borealis AG
Trademark:	Visico™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	z12nuq_Visico-LE4423-Ambicat-LE4476.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Visico LE4423 / Ambicat LE4476 is a silane crosslinkable natural compound designed for low voltage power cables up to 6 kV. The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4476 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water. When properly mixed, addition of 5 parts of Ambicat LE4476 to 95 parts of Visico LE4423 , insulation with excellent thermo-oxidative stability, also in contact with copper as well as aluminium, is achieved. If the insulation is designed to meet the thermooxidative ageing demand requiring by IEC 60502 at 150°C in contact with copper, addition of 9 parts Ambicat LE4476 to Visico LE4423 is recommended. Visico LE4423 / Ambicat LE4476 contains antioxidant, metal deactivator and a drying agent. Visico LE4423 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst. Visico LE4423 / Ambicat LE4476 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure: ASTM D 1248 Type I, Class A, Category 4 HD 603 S1 HD 604 S1 IEC 60502-1 NEMA WC 70 NEMA WC 71 The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information. The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4476 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4423 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane. The catalyst masterbatch, Ambicat LE4476 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.

Message

Visico LE4423 / Ambicat LE4476 is a silane crosslinkable natural compound designed for low voltage power cables up to 6 kV.

The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4476 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.

When properly mixed, addition of 5 parts of Ambicat LE4476 to 95 parts of Visico LE4423 , insulation with excellent thermo-oxidative stability, also in contact with copper as well as aluminium, is achieved. If the insulation is designed to meet the thermooxidative ageing demand requiring by IEC 60502 at 150°C in contact with copper, addition of 9 parts Ambicat LE4476 to Visico LE4423 is recommended.

Visico LE4423 / Ambicat LE4476 contains antioxidant, metal deactivator and a drying agent. Visico LE4423 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.

Visico LE4423 / Ambicat LE4476 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure:

ASTM D 1248 Type I, Class A, Category 4

HD 603 S1

HD 604 S1

IEC 60502-1

NEMA WC 70

NEMA WC 71

The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information.

The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4476 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4423 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane. The catalyst masterbatch, Ambicat LE4476 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.

General Information
Additive	Antioxidant Metal Deactivator Scorch Resistant
Features	Antioxidant Crosslinkable Fast Cure Good Processability Good Surface Finish Good Thermal Stability Low Die Swell Oxidation Resistant
Uses	Cable Jacketing Low Voltage Insulation
Agency Ratings	ASTM D 1248, I, Class A, Cat. 4 HD 603 S1 HD 604 S1 IEC 60502-1 NEMA WC-70 , WC-71
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density ¹	0.923	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F20)	> 96.0	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	52		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 15.0	MPa	ISO 527-2/250
Tensile Strain (Break)	> 300	%	ISO 527-2/250

Aging	Nominal Value	Unit	Test Method
Change in Tensile Properties			IEC 60811-2-1
135°C ²	< 25	%
150°C ³	< 30	%

Thermal	Nominal Value	Unit	Test Method
Hot Set			IEC 60811-2-1
200°C ⁴	60	%
200°C ⁵	0.0	%

Additional Information	Nominal Value	Unit
Crosslinking
23°C, 700.0 µm ⁶	1.5	day
23°C, 1.80 mm ⁷	7.0	day
90°C, 700.0 µm ⁸	< 15.0	min
90°C, 1.80 mm ⁹	1.00	hr

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Electric Strength	> 22	kV/mm	IEC 60243-1
Dielectric Constant (50 Hz)	< 2.30		IEC 60250
Dissipation Factor (50 Hz)	< 5.0E-4		IEC 60250

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150	°C
Cylinder Zone 2 Temp.	170	°C
Cylinder Zone 3 Temp.	170	°C
Cylinder Zone 4 Temp.	170	°C
Die Temperature	170	°C

Note Message
1 .	Mixture 95:5, ISO 1872-2
2 .	Addition of 5% Catalyst, 240 h
3 .	Addition of 9% Catalyst, 168 h
4 .	Elongation under load, 0.20 MPa
5 .	Permanent deformation, 0.20 MPa
6 .	In air, 50 % humidity
7 .	In air, 50 % humidity
8 .	Sauna or water bath
9 .	Sauna or water bath

Resin Grade	Manufacturer	Category	Trademark
Premier PPHR-810	Premier Polymers, LLC.	PP Homopolymer	Premier
NYCOA Polyamide 2248	Nycoa (Nylon Corporation of America)	Nylon 6	NYCOA Polyamide
AKROMID® B3 GK 15 natural (1824)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
Celanex® 5300-2	Celanese Corporation	PBT	Celanex®
EnCom 1016	EnCom, Inc.	PC	EnCom

Resin Grade

Manufacturer