LNP™ LUBRICOMP™ OL004 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z10cyD_LNP-LUBRICOMP-OL004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OL004 is a compound based on PPS - Linear resin containing 20% PTFE. Added features of this grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound OL-4040 Product reorder name: OL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption (24 hr, 50% RH) | 0.021 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3010 | MPa | ASTM D638 |
| -- | 3420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Break 3 | 53.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 4.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2840 | MPa | ASTM D790 |
| -- 7 | 2890 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 97.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 96.7 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 96.2 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.080 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.400 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 84.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 33 | J/m | ASTM D256 |
| 23°C 10 | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 11 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.70 | J | ASTM D3763 |
| -- | 0.900 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 99.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 102 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu N6G25 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| ExxonMobil™ HDPE HTA 002 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| INLUBE PEITF15 | Infinity LTL Engineered Compounds | PEI | INLUBE |
| LUVOCOM® 1-8068/GY-1 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hostacom CR 250 F G21259 | LyondellBasell Industries | PP, Unspecified | Hostacom |