Wellamid® FRGS25-66-NBK3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z0ir3P_Wellamid-FRGS25-66-NBK3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® FRGS25-66-NBK3 is a Polyamide 66 (Nylon 66) material filled with 25% glass bead. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Wellamid® FRGS25-66-NBK3 are:
Typical application of Wellamid® FRGS25-66-NBK3: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.0 to 1.4 | % | |
| Flow : 23°C | 1.0 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 271 to 282 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Nozzle Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI TST | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Aropol™ 10401 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Gallonprene® GP310-553A | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hyundai EP PA66 LD900 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| ICORENE® 4014 | ICO Polymers EMEA, A Division of A. Schulman | PP Copolymer | ICORENE® |