Plenco 04311 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yzOPlp_Plenco-04311-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized under component file E40654. 04311 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Apparent Density | 0.70 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9170 | MPa | ASTM D638 |
| Tensile Strength | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 8840 | MPa | ASTM D790 |
| Flexural Strength | 95.2 | MPa | ASTM D790 |
| Compressive Strength | 196 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19.9 | J/m | ASTM D256 |
| Notched Izod Impact | 17 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 190 | °C | ASTM D648 |
| Continuous Use Temperature | 206 | °C | ASTM D794 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.9E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 11 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.060 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.22%Heat Resistance, ASTM D794: 206°CDrop Ball Impact, PLENCO Method: 90 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 P-100 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Tecodur® PB70 GR30 NL MB04 | Eurotec Engineering Plastics | PBT+ASA | Tecodur® |
| NYCOA Polyamide GR30 V0 Black | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Calprene® 405 | Dynasol Elastomers | SBS | Calprene® |
| Gallonprene® GP210-7511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |