AKROMID® A3 CF 20 black (3132)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yz04dE_AKROMID-A3-CF-20-black-3132-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties Applications are mechanically strongly loaded components in all industry sectors |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.22 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 2.5 | 3.7 | % | ISO 178 |
| Tensile Modulus | 15000 | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 1.5 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 14000 | 10000 | MPa | ISO 178 |
| Flexural Stress 3 | 290 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | > 40 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 262 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 254 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 223 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 3.7E+3 | -- | ohms | IEC 60093 |
| Volume Resistivity | 4.9E+6 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOMAMID® 6M30 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Karina COMP. PVC GRAY E 800-18/695-CY-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Lusin® Clean G 320 | Chem-Trend L.P. | Unspecified | Lusin® |
| Panlite® GM-9710 | TEIJIN LIMITED | PC+Polyester | Panlite® |
| NORYL™ WCA871A resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |