Badamid® UL A70 GF30 H FR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yyqsCa_Badamid-UL-A70-GF30-H-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®UL A70 GF30 H FR is a polyamide 66 (nylon 66) material, which contains a 30% glass fiber reinforced material. This product is available in Europe,. Badamid®The main characteristics of UL A70 GF30 H FR are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.1 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 170 | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 65 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 6.0 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 262 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 4.00mm | 1.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 4.00mm | 6.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.60 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | UL 94 | |
| 1.60 mm | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 230°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 120°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silmar® SIL94BA-987A | Interplastic Corporation | Polyester, TS | Silmar® |
| EMPILON® HA40 | EMPILON | SEBS | EMPILON® |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |
| Sylvin 8370-88 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Clyrell RC5056 | PolyMirae | PP Random Copolymer | Clyrell |