WPP TPO TPO-2561 P Black
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yyY0to_WPP-TPO-TPO-2561-P-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP TPO TPO-2561 P Black is a composite polypropylene product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus - Tangent 3 | 700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Instrumented Dart Impact 4(-30°C) | 23.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 2.1E-4 | cm/cm/°C | ASTM E831 |
| Additional Information |
|---|
| Tensile Elongation at Break, ASTM D638, 50mm/min: >500% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 210 - 216 | °C | |
| Front Temperature | 216 - 227 | °C | |
| Nozzle Temperature | 210 - 227 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 10.3 | MPa | |
| Holding Pressure | 1.72 - 4.14 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 0.25 to 2.5 in/sZone 4 Temperature: 420 to 445°FHot Runner Temperature: 420 to 460°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 33 mm/min |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTARIN® C ESD 60 | Röchling Sustaplast SE & Co. KG | Acetal (POM) Copolymer | SUSTARIN® |
| VALOX™ ENH4550 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Chemlon® 66AH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hanwha Total PP WH72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LNP™ STAT-KON™ CX01039 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ STAT-KON™ |