MAJORIS DEG368X-8432 is a 35% glass fibre reinforced polypropylene high performance compound intended for injection moulding.

The product is available in natural, but other colours can be provided on request.

MAJORIS DEG368X-8432 has been developed especially for demanding applications in various engineering sectors.

MAJORIS DEG368X-8432 has high rigidity and impact strength, good dimensional stability, very good stiffness and good creep resistancy also at high temperatures.

APPLICATIONS
Product requiring very high overall mechanical performance such as:

Electrical tool and appliance components

Under the bonnet parts

Miscellaneous technical items

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Features	Good dimensional stability Rigidity, high Rigid, good Impact resistance, high Recyclable materials Good creep resistance
Uses	Electrical/Electronic Applications Power/other tools Home appliance components Parts under the hood of a car
Appearance	Available colors Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	6.0	g/10 min	ISO 1133
Molding Shrinkage			Internal method
Vertical flow direction : 2.00mm	0.80	%	Internal method
Flow direction : 2.00mm	0.30	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5500	MPa	ISO 527-2/1
Tensile Stress (Yield)	70.0	MPa	ISO 527-2/50
Tensile Strain (Break)	4.2	%	ISO 527-2/50
Flexural Modulus ¹	5650	MPa	ISO 178
Flexural Stress	122	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	52	kJ/m²	ISO 179/1eU

Injection	Nominal Value	Unit
Processing (Melt) Temp	230 - 270	°C
Mold Temperature	30.0 - 60.0	°C
Injection Rate	Moderate
Holding Pressure	30.0 - 60.0	MPa

Injection instructions
Screw speed: Low to mediumBack pressure: Low to medium

Note Message
1 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
Badaflex® TPE-S 50D 1000LD	Bada AG	TPE	Badaflex®
IPC PP 4840H-T	International Polymers Corporation	PP Homopolymer	IPC PP
LEXAN™ GF1311R resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
LONGLITE® PMC T220NA	CCP Group	Phenolic	LONGLITE® PMC
LNP™ THERMOCOMP™ RF009S compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™