Sorona® 2045G BK346A
| Category: | PTT , RENEWABLY SOURCED™ THERMOPLASTIC POLYMER* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Sorona® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yyFrmT_Sorona-2045G-BK346A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 45% Glass Reinforced Polytrimethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Melting Temperature 1 | 227 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.51 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LB01018 - C | Premier Polymers, LLC. | LLDPE | Premier |
| PRIMALENE WPP562 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Monprene® CP-37150 | Teknor Apex Company | TPE | Monprene® |
| HiFill® PC/PBT IM 5720 UV BK | Techmer Engineered Solutions | PC+PBT | HiFill® |
| LUVOCOM® 1-0889-2 | LEHVOSS Group | Nylon 66 | LUVOCOM® |