POCAN® BF 4225 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yy41s7_POCANBF4225000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 20 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.60 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 19.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 1.2 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm 3 | 0.50 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | % | ISO 2577 |
| Viscosity Number (Reduced Viscosity) | 97.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 200 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7600 | MPa | ASTM D638 |
| 23°C | 8300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture, 23°C | 119 | MPa | ASTM D638 |
| Fracture, 23°C | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638, ISO 527-2/5 |
| Flexural Modulus | |||
| 23°C | 6180 | MPa | ASTM D790 |
| 23°C 5 | 8100 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 176 | MPa | ASTM D790 |
| 23°C 6 | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength (23°C) 7 | 3.1 | % | ISO 178/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| Electric Strength | 12.4 | °C | IEC 60216 |
| Tensile Impact Strength | 9.2 | °C | IEC 60216 |
| Tensile Strength | 11.7 | °C | IEC 60216 |
| Temperature index | IEC 60216 | ||
| Electric Strength, 20000 hr | 145 | °C | IEC 60216 |
| Tensile Impact Strength, 20000 hr | 135 | °C | IEC 60216 |
| Tensile Strength, 20000 hr | 140 | °C | IEC 60216 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GFHMR, 07-080, GF20; ISO 1043-PBT GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.12 0.0 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | ISO 180/1U |
| 23°C | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.23 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.80 | IEC 60250 | |
| 23°C, 1 MHz | 3.60 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 725 | °C | IEC 60695-2-13 |
| 1.50 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 725 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 4.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3463 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Borealis PP HG385MO | Borealis AG | PP Homopolymer | Borealis PP |
| Karina IVORY PVC COMPOUND 939-35/ 1-CY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 110 01 V0 | LOXIM Industries Private Limited | PC | LOXIM |
| SABIC® PP 500P | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |