TAROPRENE® 2 A80 E1G
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROPRENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxwXqL_TAROPRENE-2-A80-E1G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Elastomer Vulcanized. This TPE-V compound combines the typical performance of a vulcanized elastomer with the easy processing of a thermoplastic compound. Taroprene is totally recyclable and it can be produced in standard grades and in tailor-made grades. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 80 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 3.65 | MPa | |
| 300% Strain | 5.28 | MPa | |
| Tensile Strength 2(Break) | 8.60 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 640 | % | ASTM D412 |
| Tear Strength | 41.6 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 47 | % | |
| 100°C, 22 hr | 58 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Die C |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3569 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Royalcast® 3109 | Chemtura | PUR-Ether | Royalcast® |
| 4MID® 9B22130 HUV | 4Plas | Nylon 6 | 4MID® |
| ATPioneers Acrylic ACN 102 | Asia Technology Pioneers Ltd | Acrylic, Unspecified | ATPioneers Acrylic |
| LG ABS AF366 | LG Chem Ltd. | ABS | LG ABS |