EPO-TEK® 320NC
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxhwpH_EPO-TEK-320NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, black-colored and optically opaque epoxy designed for optical, medical, and opto-electronic packaging of semiconductor devices and components. It is a modification of EPO-TEK ® 320 for increased insulation and dielectric properties. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 340 | °C | |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 175 | °C | |
| Intermittent | -55 to 275 | °C | |
| Storage Modulus (23°C) | 3.71 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.39 | % | |
| 250°C | 0.63 | % | |
| 300°C | 1.3 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 50.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.8E-5 | cm/cm/°C | |
| -- 3 | 9.4E-5 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance (300 to 2500 nm) | < 1.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Black | ||
| -- 5 | Clear/Transparent | ||
| Density | |||
| Part B | 0.878 | g/cm³ | |
| Part A | 2.05 | g/cm³ | |
| Viscosity 6(23°C) | 1.0 to 3.0 | Pa·s | |
| Curing Time (70°C) | 1.0 | hr | |
| Pot Life | 20 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 9.92 | ||
| Volume Resistivity (23°C) | > 2.0E+11 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.067 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR50 NL HS | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| VESTAMID® HTplus M3033 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| TOTAL Polypropylene PPC 4820WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Huafon JF-PDY-515Y | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 4250-50 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |