SABIC® PPcompound 55T1030S
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxNYGK_SABIC-PPcompound-55T1030S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 55T1030S is a Polypropylene copolymer with 30% talcum. It is especially suited for applications that require an exceptional stiffness combined with a high impact resistance (even at low temperatures) like dashboard carriers and other dashboard components that are exposed to high temperatures. SABIC® PPcompound 55T1030 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 24.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 18.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 80 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 13 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 3.5 | kJ/m² | |
| 0°C, Injection Molded | 6.0 | kJ/m² | |
| 23°C, Injection Molded | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 7.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 3554 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| ELASTOSIL® RT 601 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| En Chuan 336T | En Chuan Chemical Industries Co,. Ltd. | PS (GPPS) | En Chuan |
| Polifor® C 25 TR/25 UV GRIGIO 7437 | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Sumiliteresin® PR-13349 | SBHPP | Phenolic | Sumiliteresin® |