Akulon® S223-PG8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxHiqz_Akulon-S223-PG8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® S223-PG8 is a Polyamide 66 (Nylon 66) material filled with 40% glass fiber. It is available in Europe. Primary attribute of Akulon® S223-PG8: Impact Modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 4.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 175 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 5.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 14 | kJ/m² | |
| 23°C | 20 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 100 | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 14.0 | ||
| 1 MHz | 3.30 | 4.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 9.0E-3 | 0.30 | ||
| 1 MHz | 0.015 | 0.12 | ||
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 295 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K4535 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| VisiJet® FTI Blue | 3D Systems | Unspecified | VisiJet® |
| Gallonprene® GP520-8011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA4/6 CF30 TL10 | Techmer Engineered Solutions | Nylon 46 | Plaslube® |