API PS 505
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | American Polymers, Inc. |
| Trademark: | API PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxBiMk_API-PS-505.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
API 505 is an intermediate grade of impact modified polystyrene. This material has exceptional moldability and colorability. Application: API 505 is widely used in the manufacture housewares, toys, containers, displays, and a wide range of injection molded applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 59 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength (Break) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 177 to 232 | °C | |
| Front Temperature | 191 to 274 | °C | |
| Mold Temperature | -6.67 to 71.1 | °C | |
| Injection Pressure | 34.5 to 276 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502BZ | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| RAMLLOY PN300G6 | Polyram Ram-On Industries | PPE+PS | RAMLLOY |
| VeroGray™ RGD850 | Stratasys | Unspecified | VeroGray™ |
| VITAMIDE® TR36BK6635 | Jackdaw Polymers | Nylon 66/6 | VITAMIDE® |
| Latilub 66-02S | LATI S.p.A. | Nylon 66 | Latilub |