InnoTuf® TP-4016
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yvtrlm_InnoTuf-TP-4016.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4016 is an impact resistant polyurethane formulated for room temperature meter-mix dispensing systems. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. TP 4016 is a U.L. 94v1 registered flame retardant polyurethane. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.22 | g/cm³ | |
| Cured | 1.25 | g/cm³ | |
| Hardener | 1.28 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 44.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 50 Mix Ratio by Weight: 52 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 120 to 240 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.20 | Pa·s | |
| 38°C 2 | 0.35 | Pa·s | |
| 38°C 3 | 0.70 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 5.0 to 7.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Modulus | 689 | MPa | ASTM D638 |
| Tensile Strength | 46.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 1 hour at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANTEC PC S90R | Polykemi AB | PC | SCANTEC |
| XANTAR® C CM 406 | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| Network Polymers HDPE 50 0149 | Network Polymers, Inc. | EHMWPE | Network Polymers HDPE |
| KRALASTIC® AN-450 | Nippon A&L Inc. | ABS | KRALASTIC® |
| Infino XP-2165M | SAMSUNG SDI CO., LTD. | PPS | Infino |