RTP 2287 HEC
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yvoGTS_RTP-2287-HEC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nickel-Coated Carbon Fiber - EMI/RFI Shielding - Electrically Conductive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.050 | % | ASTM D955 |
| Moisture Content | 0.10 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20700 | MPa | ASTM D638 |
| Tensile Strength | 193 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 19300 | MPa | ASTM D790 |
| Flexural Strength | 283 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 300 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+3 | ohms | ASTM D257 |
| -- | < 1.0E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 163 - 218 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| Remove hopper magnets.Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F101FR | Mando Advanced Materials Co., Ltd. | PBT | TEKASTER™ |
| WACKER® W 23 SILICONE WAX | Wacker Chemie AG | Silicone | WACKER® |
| Iupilon® EFR2150 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| MAJORIS AT360 | AD majoris | PP Copolymer | MAJORIS |
| OLEFISTA™ QX0238E | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |