Witcom PP C/2S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yv3G7G_Witcom-PP-C-2S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PP C/2S is a polypropylene product that contains stainless steel fibers. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 - 2.0 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 225 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 10 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 70.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| EMI Shielding Effectiveness (3.00 mm) | 40.0 - 55.0 | dB | ASTM D4935 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 200 - 245 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® HT 60 | API SpA | SEBS | megol® |
| NEO-ZEX™ 0134L | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| 4PROP® 9D02430 HUV | 4Plas | PP Homopolymer | 4PROP® |
| Axiall PVC 19901 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hapflex™ 669 | Hapco Inc. | TP, Unspecified | Hapflex™ |