Durethan® BKV 15 G H2.0 900051
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yuoOa9_Durethan-BKV-15-G-H2-0-900051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, 15 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, weather stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.24 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 3.00 mm 1 | 0.67 | -- | % | |
| Across Flow : 120°C, 4 hr, 3.00 mm 2 | 0.21 | -- | % | |
| Flow : 280°C, 3.00 mm 3 | 0.34 | -- | % | |
| Flow : 120°C, 4 hr, 3.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 190 | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 6310 | 3880 | MPa | ASTM D638 |
| 23°C | 6300 | 4000 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 117 | 67.6 | MPa | ASTM D638 |
| Break, 23°C | 120 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 3.0 | 11 | % | ASTM D638, ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 5700 | 3500 | MPa | ASTM D790 |
| 23°C 5 | 5700 | 3500 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 185 | 125 | MPa | ASTM D790 |
| 3.5% Strain, 23°C | -- | 100 | MPa | ISO 178/A |
| 23°C 6 | 185 | 125 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 7.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66, GHR, 14-060, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | 35 | kJ/m² | |
| 23°C | 40 | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 20 | 25 | kJ/m² | |
| 23°C | 25 | 35 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.50 | -- | J | |
| 23°C | 2.00 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 505 | -- | N | |
| 23°C | 560 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 9 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.10 | 10.0 | ||
| 23°C, 1 MHz | 3.70 | 4.30 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 8.0E-3 | 0.22 | ||
| 23°C, 1 MHz | 0.018 | 0.070 | ||
| Comparative Tracking Index (Solution A) | 375 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 10 | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/TP-GP3-G10 | Polymer Resources Ltd. | PC+Polyester | PRL |
| SLOVAMID® 6 GF 5 T 20 FRG 2 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TOTAL Polyethylene EVA 1040 VN 4 | TOTAL Refining & Chemicals | EVA | TOTAL Polyethylene |
| Novalloy-A A5622 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| INSTRUC PA12GF30 | Infinity LTL Engineered Compounds | Nylon 12 | INSTRUC |