LNP™ STAT-KON™ RD000 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yuUaRp_LNP-STAT-KON-RD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* RD000 is a compound based on Nylon 66 resin containing Carbon Powder. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound R Product reorder name: RD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.7 | % | |
| Across Flow : 24 hr | 2.4 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.54 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.96 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3170 | MPa | ASTM D638 |
| -- | 3100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 67.5 | MPa | ASTM D638 |
| Break | 64.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.5 | % | ASTM D638 |
| Break | 7.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 95.7 | MPa | ASTM D790 |
| -- | 96.4 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 7.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 90 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.80 | J | ASTM D3763 |
| -- | 3.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 94.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 77.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6785 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Maxelast® S4750 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Colorite Rigid PVC 2690 CLR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Flexane® 94 Liquid | Devcon | PUR, Unspecified | Flexane® |
| POLIMAXX 2300SC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |