LNP™ THERMOTUF™ VF008 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yuH36P_LNP-THERMOTUF-VF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF VF008 is a compound based on Super Tough Nylon resin containing 40% Glass Fiber. Added feature of this material is: High Impact. Also known as: LNP* THERMOTUF* Compound VF-1008 Product reorder name: VF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.38 | g/cm³ | |
| -- | 1.40 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.45 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.66 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 126 | MPa | ASTM D638 |
| Break | 127 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 3.3 | % | ASTM D638 |
| Break | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 8600 | MPa | ASTM D790 |
| -- 4 | 8540 | MPa | ISO 178 |
| Flexural Strength 5(Break, 50.0 mm Span) | 194 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 6 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 7 | 58 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.80 | J | ASTM D3763 |
| -- | 5.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 258 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 245 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 238 | °C | ISO 75-2/Af |
| CLTE - Flow (-40 to 40°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.38 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 183 HEC | RTP Company | PP, Unspecified | RTP |
| Moplen EP200R | PolyMirae | TPU, Unspecified | Moplen |
| Nylfor® A2 E6/3E NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Geon™ Vinyl Flexible R328BE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| TECHNYL® C 216 V30 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |