UNIVAL™ DMDF-6230 NT
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yu9w4K_UNIVAL-DMDF-6230-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
UNIVAL™ DMDF-6230 NT High Density Polyethylene (HDPE) Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 20 gallons in size -applications that require the combination of outstanding environmental stress crack resistance (ESCR) and, high impact strength. UNIVAL DMDF- 6230 NT HDPE resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids. In addition, it can be blow molded into other thin walled parts and houseware items, and also can be extruded into profiles or sheets. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 180 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 23.4 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 900 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 910 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 210 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 130 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 118 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8874-81C NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Fainplast CTX 70/S | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Fainplast |
| K-vinyl 70 Deg C Rating Insulation (85-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Jam PE 534F7 | Jam Petrochemical Company | HDPE | Jam PE |
| SHINSTRA AG20TKB (PA66) | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |