VENYL SB802
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yu0a1Z_VENYL-SB802.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SB802 is a natural, high mineral filled polyamide 6 intended for injection moulding. APPLICATIONS VENYL SB802 has been developed for applications where high density, good surface finish are necessary. High density products, such as : Sound absorption parts, electronic housings, cosmetics mouldings, appliances VENYL SB802 is available in both natural (VENYL SB802) and black (VENYL SB802-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.90 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 41.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7350 | MPa | ISO 178 |
| Flexural Stress | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 8.4 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 85.0 to 110 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ 34-1520 UV SSM TFPP | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Reny® 1722F | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| HANWHA KH-31G | Hanwha Chemical | PVC, Unspecified | HANWHA |
| OTECH PVC OW135 - Riser Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 5221-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |