CYCOLAC™ DL200H resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ytZxv1_CYCOLACDL200Hresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLAC DL200H is a hydrostable high heat ABS/PC blend |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 260°C/5.0 kg | 25 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2330 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/50 |
| Fracture | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 3.9 | % | ISO 527-2/50 |
| Fracture 3 | 70 | % | ASTM D638 |
| Fracture | 75 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 4 | 2200 | MPa | ASTM D790 |
| -- 5 | 2100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 75.0 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 30 | kJ/m² | ISO 179/1eA |
| 23°C | 65 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 620 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 500 | J/m | ASTM D256 |
| -40°C 8 | 21 | kJ/m² | ISO 180/1A |
| 23°C 9 | 56 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 120 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 101 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 96.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 - 104 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 249 - 282 | °C | |
| Middle Temperature | 254 - 288 | °C | |
| Front Temperature | 254 - 288 | °C | |
| Nozzle Temperature | 260 - 288 | °C | |
| Processing (Melt) Temp | 260 - 288 | °C | |
| Mold Temperature | 76.7 - 98.9 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP541K | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Sinvicomp SZF4669A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| CEPLA CT-253 | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| DOWLEX™ 2032 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| LUVOCOM® 65/XCF/30 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |