VALOX™ K4530 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ysgn4p_VALOXK4530resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.70 - 0.90 | % | Internal method |
| Transverse flow : 3.20mm | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3560 | MPa | ASTM D638 |
| -- | 5250 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 103 | MPa | ASTM D638 |
| Yield | 98.0 | MPa | ISO 527-2/5 |
| Fracture | 97.2 | MPa | ASTM D638 |
| Fracture 3 | 103 | MPa | ASTM D638 |
| Fracture | 89.6 | MPa | ASTM D638 |
| Fracture | 82.0 | MPa | ASTM D638 |
| Fracture | 98.0 | MPa | ASTM D638 |
| Fracture | 98.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 7.0 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2/5 |
| Fracture | 2.3 | % | ASTM D638 |
| Fracture | 4.0 | % | ASTM D638 |
| Fracture | 2.5 | % | ASTM D638 |
| Fracture | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span | 4820 | MPa | ASTM D790 |
| 50.0mm span | 5100 | MPa | ASTM D790 |
| 50.0mm span | 4530 | MPa | ASTM D790 |
| 50.0mm span | 4810 | MPa | ASTM D790 |
| 50.0mm span 5 | 4640 | MPa | ASTM D790 |
| -- 6 | 4750 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Fracture, 50.0mm span 7 | 150 | MPa | ASTM D790 |
| Bending strain- 1.3 mm/min, 50 mm span | ASTM D790 | ||
| -- 8 | 7.0 | % | ASTM D790 |
| -- 9 | 6.0 | % | ASTM D790 |
| -- 10 | 3.8 | % | ASTM D790 |
| -- 11 | 9.7 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 58 | J/m | ASTM D256 |
| 23°C 12 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 13 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, Total Energy 14 | 4.97 | J | ASTM D3763 |
| 23°C, Total Energy 15 | 5.30 | J | ASTM D3763 |
| 23°C, Total Energy 16 | 6.10 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 193 | °C | ASTM D648 |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 76.7 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | AFTER 1008 HOURS AT 125°C |
| 9 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 10 . | AFTER 1008 HOURS AT 155°C |
| 11 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 15 . | AFTER 1008 HOURS AT 125°C |
| 16 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC4PAZ (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Viprene™ G40D-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Vyncolit® 2061B | Vyncolit N.V. | Epoxy | Vyncolit® |
| WPP PP PPH5GF2-7894 Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| DuPont™ Entira™ AS MK400 | DuPont Packaging & Industrial Polymers | Ionomer | DuPont™ Entira™ |