Jamplast JPSANC
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ysLa3I_Jamplast-JPSANC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Jamplast JPSANC SAN (styrene-acrylonitrile) resins are thermoplastic materials that provide an excellent balance of processability, clarity, chemical and heat resistance and stiffness. JPSANC SAN resins can be injection molded, extruded, blended with ABS or PVC, or used as color concentrate carriers. Jamplast SAN resins are primarily used for blending with ABS or rigid PVC resins and are also used as carriers for making color concentrates. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3590 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 55.6 | MPa | |
| Break | 55.6 | MPa | |
| Tensile Elongation 3(Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 4270 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 99.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 101 | °C | |
| 0.45 MPa, Annealed | 103 | °C | |
| 1.8 MPa, Unannealed | 87.2 | °C | |
| 1.8 MPa, Annealed | 101 | °C | |
| Vicat Softening Temperature | 113 | °C | ASTM D1525 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 93.9 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 149 to 204 | °C | |
| Front Temperature | 191 to 232 | °C | |
| Mold Temperature | -1.11 to 87.8 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP563S | PolyMirae | PP Homopolymer | Moplen |
| Clariant ABS ABS4590 | Clariant Corporation | ABS | Clariant ABS |
| Ecomass® 4703ZD84 | Ecomass Technologies | TPU, Unspecified | Ecomass® |
| MAJORIS ET212 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| LEXAN™ ML7667 resin | SABIC Innovative Plastics | PC | LEXAN™ |