ELITE™ 5400G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ysGhOc_ELITE-5400G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5400G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking tendencies for good performance on automated packaging equipment.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 6.67 | J | Internal method |
| Film Puncture Force | 68.9 | N | Internal method |
| Film Puncture Resistance | 32.3 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 83.6 | J/cm³ | ASTM D882 |
| TD | 95.1 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 218 | MPa | ASTM D882 |
| 2% secant, MD | 188 | MPa | ASTM D882 |
| 1% secant, TD | 251 | MPa | ASTM D882 |
| 2% secant, TD | 209 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 10.4 | MPa | ASTM D882 |
| TD : Yield | 10.5 | MPa | ASTM D882 |
| MD : Fracture | 38.5 | MPa | ASTM D882 |
| TD : Fracture | 36.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 450 | % | ASTM D882 |
| TD : Fracture | 630 | % | ASTM D882 |
| Dart Drop Impact | 470 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 280 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 32 | ASTM D2457 | |
| Haze | 20 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度： 409°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：39 rpm 冷冻线高度：38 英寸 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide B28 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Flexirene® MR 50 A | Versalis S.p.A. | LLDPE | Flexirene® |
| HiFill FR® PA4/6 FR HS | Techmer Engineered Solutions | Nylon 46 | HiFill FR® |
| INEOS LDPE 28H430 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| Wuxi Jiahong EB-2071A | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |