VENYL VG200 - 8716
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ys1FoR_VENYL-VG200---8716.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL VG200 - 8716 is a Polyamide 66/6 Copolymer (Nylon 66/6) product filled with 20% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 | % | |
| Water Absorption | |||
| Saturation, 23°C | 8.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 6000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 242 | °C | ISO 3146 |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | cm/cm/°C | DIN 52328 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | DIN 53480 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 255 to 265 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 265 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 85.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-86-K902A | Teknor Apex Company | TPE | Telcar® |
| WELLAMID Nylon 6600 TLWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| ACCUCOMP™ GS0500L | ACLO Compounders Inc. | PS (GPPS) | ACCUCOMP™ |
| BCC Resins MB 2000 | BCC Products Inc. | TS, Unspecified | BCC Resins |
| Geon™ Vinyl Flexible C75A0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |