Paxon™ BU46-060
| Category: | HDPE, UHMW , High Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Paxon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yqP4wP_Paxon-BU46-060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BU46-060 is a high molecular weight high density polyethylene copolymer, which contains an anti-ultraviolet agent. It has good processability, excellent melting strength, high impact strength, chemical resistance and high stress cracking resistance. It is often used for co-extrusion purposes. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 6.3 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 23.0 | MPa | ASTM D638 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 67-01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| VENYL SFRHWGT300H - 8229 | AD majoris | Nylon 6 | VENYL |
| Durez® 25378 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Karina IVORY PVC COMPOUND 70900-35/ 1-F-AC-HSF-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina NATURAL PVC COMPOUND -E 730D25/ 1-IS-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |