| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yplkQb_Hifax-DG-232-2693.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| HIFAX DG232 2693 is a high impact, medium flow, rubber modified grade for use in Automotive applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 16.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | > 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | > 7.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HIDEN® P603H U | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| POLYFLON™ F-208 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Infino LX-1080 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |
| SIBUR Synthetic Rubber IR SKI-3 NST Group I | SIBUR | IR | SIBUR Synthetic Rubber |
| ULTEM™ 2310 resin | SABIC Innovative Plastics | PEI | ULTEM™ |