SABIC® LDPE 2008N0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ypM00u_SABIC-LDPE-2008N0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2008N0 is a LDPE tubular grade without additives. SABIC® LDPE 2008TN00 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application SABIC® LDPE 2008N0 is typically suitable for injection moulding application, frequently used for caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | |
| 190°C/5.0 kg | 28 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 10.0 | cm³/10min | |
| 190°C/5.0 kg | 33.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 40 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 130 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, Injection Molded | 8.00 | MPa | |
| Break, Injection Molded | 10.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 120 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 9.0 | kJ/m² | |
| 23°C, Injection Molded | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 43.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 107 | °C | DIN 53765 |
| Enthalpy Change | 125 | J/g | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3811 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Delrin® PC652 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Durethan® DP 2131/20 H2.0 900051 | LANXESS GmbH | Nylon 6 | Durethan® |
| POLYform C M20 UV | Polykemi AB | Acetal (POM) Copolymer | POLYform C |
| Hostacom TRC 787N E1 G81493 | LyondellBasell Industries | PP Copolymer | Hostacom |