VECTRA® E840i LDS
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yoOSw2_VECTRA-E840i-LDS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% Mineral filled Laser Direct Structuring grade. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in black at 1.5mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.81 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.011 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 4.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 102 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 33 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 227 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 4.97 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.029 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 340 - 350 | °C | |
| Processing (Melt) Temp | 340 - 350 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 340 to 350°CZone 4 Temperature: 335 to 345°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V975 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tarnoform® 300 GF2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| 4LAC® 10H20800 | 4Plas | ABS | 4LAC® |
| Kynar Flex® 2750-01 | Arkema | PVDF | Kynar Flex® |
| LNP™ LUBRICOMP™ KAL22 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |